A sample of bismuth strontium calcium copper oxide (BSCCO), which is currently one of the most practical high-temperature superconductors. Notably, it does not contain rare earths. BSCCO is a cuprate superconductor based on bismuth and strontium. Thanks to its higher operating temperature, cuprates are now becoming competitors for more ordinary niobium-based superconductors, as well as magnesium diboride superconductors.

High-temperature superconductivity (high-Tc or HTS) is superconductivity in materials with a critical temperature (the temperature below which the material behaves as a superconductor) above 77 K (−196.2 °C; −321.1 °F), the boiling point of liquid nitrogen.[1] They are "high-temperature" only relative to previously known superconductors, which function only closer to absolute zero. The first high-temperature superconductor was discovered in 1986 by IBM researchers Georg Bednorz and K. Alex Müller.[2][3] Although the critical temperature is around 35.1 K (−238.1 °C; −396.5 °F), this material was modified by Ching-Wu Chu to make the first high-temperature superconductor with critical temperature 93 K (−180.2 °C; −292.3 °F).[4] Bednorz and Müller were awarded the Nobel Prize in Physics in 1987 "for their important break-through in the discovery of superconductivity in ceramic materials".[5] Most high-Tc materials are type-II superconductors.

The major advantage of high-temperature superconductors is that they can be cooled using liquid nitrogen,[2] in contrast to previously known superconductors, which require expensive and hard-to-handle coolants, primarily liquid helium. A second advantage of high-Tc materials is they retain their superconductivity in higher magnetic fields than previous materials. This is important when constructing superconducting magnets, a primary application of high-Tc materials.

The majority of high-temperature superconductors are ceramics, rather than the previously known metallic materials. Ceramic superconductors are suitable for some practical uses but encounter manufacturing issues. For example, most ceramics are brittle, which complicates wire fabrication.[6]

The main class of high-temperature superconductors is copper oxides combined with other metals, especially the rare-earth barium copper oxides (REBCOs) such as yttrium barium copper oxide (YBCO). The second class of high-temperature superconductors in the practical classification is the iron-based compounds.[7][8] Magnesium diboride is sometimes included in high-temperature superconductors: It is relatively simple to manufacture, but it superconducts only below Template:Cvt, which makes it unsuitable for liquid nitrogen cooling.

History

[edit | edit source]
File:Timeline of Superconductivity from 1900 to 2015.svg
Timeline of superconductor discoveries. On the right is the liquid nitrogen temperature, which usually divides superconductors at high from superconductors at low temperatures. Cuprates are displayed as blue diamonds, and iron-based superconductors as yellow squares. Magnesium diboride and other low-temperature or high-pressure metallic BCS superconductors are displayed for reference as green circles.

Superconductivity was discovered by Kamerlingh Onnes in 1911, in a metal solid. Ever since, researchers have attempted to create superconductivity at higher temperatures[9] with the goal of finding a room-temperature superconductor.[10] By the late 1970s, superconductivity was observed in several metallic compounds (in particular Nb-based, such as NbTi, Nb3Sn, and Nb3Ge) at temperatures that were much higher than those for elemental metals and which could even exceed 20 K (−253.2 °C).

In 1986, at the IBM research lab near Zürich in Switzerland, Bednorz and Müller were looking for superconductivity in a new class of ceramics: the copper oxides, or cuprates. In that year, Bednorz and Müller discovered superconductivity in lanthanum barium copper oxide (LBCO), a lanthanum-based cuprate perovskite material, which had a transition temperature of 35 K (Nobel Prize in Physics, 1987).[11] It was soon found that replacing the lanthanum with yttrium (i.e., making YBCO) raised the critical temperature above 90 K.[12] Their results were soon confirmed[13] by many groups.[14]

In 1987, Philip W. Anderson gave the first theoretical description of these materials, based on the resonating valence bond (RVB) theory,[15] but a full understanding of these materials is still developing today. These superconductors are now known to possess a d-wave[clarification needed] pair symmetry. The first proposal that high-temperature cuprate superconductivity involves d-wave pairing was made in 1987 by N. E. Bickers, Douglas James Scalapino and R. T. Scalettar,[16] followed by three subsequent theories in 1988 by Masahiko Inui, Sebastian Doniach, Peter J. Hirschfeld and Andrei E. Ruckenstein,[17] using spin-fluctuation theory, and by Claudius Gros, Didier Poilblanc, Maurice T. Rice and FC. Zhang,[18] and by Gabriel Kotliar and Jialin Liu identifying d-wave pairing as a natural consequence of the RVB theory.[19] The confirmation of the d-wave nature of the cuprate superconductors was made by a variety of experiments, including the direct observation of the d-wave nodes in the excitation spectrum through angle resolved photoemission spectroscopy (ARPES), the observation of a half-integer flux in tunneling experiments, and indirectly from the temperature dependence of the penetration depth, specific heat and thermal conductivity.

Until 2001 the cuprates were thought be the only true high temperature superconductors. In that year MgB2 with Tc of 39K was discovered by Akimitsu and colleagues. This was followed in 2006 by Hosono and coworkers with iron-based layered oxypnictide compound with Tc of 56K.[20] These temperature are below the cuprates but well above the conventional superconductors.[21]

In 2014, evidence showing that fractional particles can happen in quasi two-dimensional magnetic materials was reported by École Polytechnique Fédérale de Lausanne (EPFL) scientists[22] lending support for Anderson's theory of high-temperature superconductivity.[23] In 2014 and 2015, hydrogen sulfide (H
2S) at extremely high pressures (around 150 gigapascals) was first predicted and then confirmed to be a high-temperature superconductor with a transition temperature of 80 K.[24][25][26]

In 2018, a research team from the Department of Physics, Massachusetts Institute of Technology, discovered superconductivity in bilayer graphene with one layer twisted at an angle of approximately 1.1 degrees with cooling and applying a small electric charge. Even if the experiments were not carried out in a high-temperature environment, the results are correlated less to classical but high temperature superconductors, given that no foreign atoms needed to be introduced.[27] The superconductivity effect came about as a result of electrons twisted into a vortex between the graphene layers, called "skyrmions". These act as a single particle and can pair up across the graphene's layers, leading to the basic conditions required for superconductivity.[28]

In 2019 it was discovered that lanthanum hydride (LaH
10) becomes a superconductor at 250 K under a pressure of 170 gigapascals.[29][26]

In 2020, a room-temperature superconductor (critical temperature 288 K) made from hydrogen, carbon and sulfur under pressures of around 270 gigapascals was described in a paper in Nature.[30][31] However, in 2022 the article was retracted by the editors because the validity of background subtraction procedures had been called into question. All nine authors maintain that the raw data strongly support the main claims of the paper.[32]

As of 2021,[33] the superconductor with the highest transition temperature at ambient pressure was the cuprate of mercury, barium, and calcium, at around Template:Cvt.[34] Other superconductors have higher recorded transition temperatures – for example lanthanum superhydride at Template:Cvt, but these only occur at high pressure.[35]

In 2023 a study reported superconductivity at room temperature and ambient pressure in highly oriented pyrolytic graphite with dense arrays of nearly parallel line defects.[36]

Selected list of superconductors

[edit | edit source]

Template:Legend2 Template:Legend2

Selection of confirmed superconductors and common cooling agents[37]
Tc/Tboiling Pressure
above ambient 		Material Notes
K °C
273.15 0 Ice: Melting point at atmospheric pressure (common cooling agent; for reference)
250 −23 170 GPa LaH10[38] Metallic superconductor with one of the highest known critical temperatures
203 −70 155 GPa High pressure phase of hydrogen sulfide (H2S) Mechanism unclear, observable isotope effect[39]
194.6 −78.5 Carbon dioxide (dry ice): Sublimation point at atmospheric pressure (common cooling agent; for reference)
151 −122 HgBa2Ca2Cu3O8+δ[40] High-temperature superconductors with copper oxide with relatively high critical temperatures
138 −135 Hg12Tl3Ba30Ca30Cu45O127[33]
110 −163 Bi2Sr2Ca2Cu3O10 (BSCCO)
92 −181 YBa2Cu3O7 (YBCO)
87 −186 Argon: Boiling point at atmospheric pressure (common cooling agent; for reference)
77 −196 Nitrogen: Boiling point at atmospheric pressure (common cooling agent; for reference)
45 −228 SmFeAsO0.85F0.15 Low-temperature superconductors with relatively high critical temperatures
41 −232 CeOFeAs
39 −234 MgB2 Metallic superconductor with relatively high critical temperature at atmospheric pressure
30 −243 La2−xBaxCuO4[41] First high-temperature superconductor with copper oxide, discovered by Bednorz and Müller
27 −246 Neon: Boiling point at atmospheric pressure (common cooling agent; for reference)
21.15 −252 Hydrogen: Boiling point at atmospheric pressure (common cooling agent; for reference)
18 −255 Nb3Sn[41] Metallic low-temperature superconductors with technical relevance
9.2 −264.0 NbTi[42]
4.21 −268.94 Helium: Boiling point at atmospheric pressure (common cooling agent of low temperature physics; for reference)
4.15 −269.00 Hg (Mercury)[43] Metallic low-temperature superconductors
1.09 −272.06 Ga (Gallium)[43]

Properties

[edit | edit source]

The "high-temperature" superconductor class has had many definitions.

The label high-Tc should be reserved for materials with critical temperatures greater than the boiling point of liquid nitrogen. However, a number of materials – including the original discovery and recently discovered pnictide superconductors – have critical temperatures below Template:Cvt but nonetheless are commonly referred to in publications as high-Tc class.[44][45]

A substance with a critical temperature above the boiling point of liquid nitrogen, together with a high critical magnetic field and critical current density (above which superconductivity is destroyed), would greatly benefit technological applications. In magnet applications, the high critical magnetic field may prove more valuable than the high Tc itself. Some cuprates have an upper critical field of about 100 tesla. However, cuprate materials are brittle ceramics that are expensive to manufacture and not easily turned into wires or other useful shapes. Furthermore, high-temperature superconductors do not form large, continuous superconducting domains, rather clusters of microdomains within which superconductivity occurs. They are therefore unsuitable for applications requiring actual superconductive currents, such as magnets for magnetic resonance spectrometers.[46] For a solution to this (powders), see HTS wire.

There has been considerable debate regarding high-temperature superconductivity coexisting with magnetic ordering in YBCO,[47] iron-based superconductors, several ruthenocuprates and other exotic superconductors, and the search continues for other families of materials. HTS are Type-II superconductors, which allow magnetic fields to penetrate their interior in quantized units of flux, meaning that much higher magnetic fields are required to suppress superconductivity. The layered structure also gives a directional dependence to the magnetic field response.

All known high-Tc superconductors are Type-II superconductors. In contrast to Type-I superconductors, which expel all magnetic fields due to the Meissner effect, Type-II superconductors allow magnetic fields to penetrate their interior in quantized units of flux, creating "holes" or "tubes" of normal metallic regions in the superconducting bulk called vortices. Consequently, high-Tc superconductors can sustain much higher magnetic fields.

Cuprates

[edit | edit source]
page-not-found

Iron-based

[edit | edit source]
Main article: Iron-based superconductor
File:Phase diagram of the 122 family of ferro-pnictides.png
Phase diagram for high-temperature superconductors based on iron[48]

Iron-based superconductors contain layers of iron and a pnictogen – such as arsenic or phosphorus – , a chalcogen, or a crystallogen. This is currently the family with the second highest critical temperature, behind the cuprates. Interest in their superconducting properties began in 2006 with the discovery of superconductivity in LaFePO at Template:Cvt[49] and gained much greater attention in 2008 after the analogous material LaFeAs(O,F)[50] was found to superconduct at up to Template:Cvt under pressure.[51] The highest critical temperatures in the iron-based superconductor family exist in thin films of FeSe,[52][53][54] where a critical temperature in excess of Template:Cvt was reported in 2014.[55]

Since the original discoveries several families of iron-based superconductors have emerged:

  • LnFeAs(O,F) or LnFeAsO1−x (Ln=lanthanide) with Tc up to Template:Cvt, referred to as 1111 materials.[8] A fluoride variant of these materials was subsequently found with similar Tc values.[56]
  • (Ba,K)Fe2As2 and related materials with pairs of iron-arsenide layers, referred to as 122 compounds. Tc values range up to Template:Cvt.[57][58] These materials also superconduct when iron is replaced with cobalt.
  • LiFeAs and NaFeAs with Tc up to around Template:Cvt. These materials superconduct close to stoichiometric composition and are referred to as 111 compounds.[59][60][61]
  • FeSe with small off-stoichiometry or tellurium doping.[62]
  • LaFeSiH with Tc around Template:Cvt in its stoichiometric composition.[63] This superconducting crystallogenide has oxide and fluoride variants LaFeSiOx and LaFeSiFx.[64][65]

Most undoped iron-based superconductors show a tetragonal-orthorhombic structural phase transition followed at lower temperature by magnetic ordering, similar to the cuprate superconductors.[66] However, they are poor metals rather than Mott insulators and have five bands at the Fermi surface rather than one.[48] The phase diagram emerging as the iron-arsenide layers are doped is remarkably similar, with the superconducting phase close to or overlapping the magnetic phase. Strong evidence that the Tc value varies with the As–Fe–As bond angles has already emerged and shows that the optimal Tc value is obtained with undistorted FeAs4 tetrahedra.[67] The symmetry of the pairing wavefunction is still widely debated, but an extended s-wave scenario is currently favoured.

Magnesium diboride

[edit | edit source]

Magnesium diboride is occasionally referred to as a high-temperature superconductor[68] because its Tc value of Template:Cvt is above that historically expected for BCS superconductors. However, it is more generally regarded as the highest Tc conventional superconductor, the increased Tc resulting from two separate bands being present at the Fermi level.

Carbon-based

[edit | edit source]

In 1991 Hebard et al. discovered Fulleride superconductors,[69] where alkali-metal atoms are intercalated into C60 molecules.

In 2008 Ganin et al. demonstrated superconductivity at temperatures of up to Template:Cvt for Cs3C60.[70]

P-doped Graphane was proposed in 2010 to be capable of sustaining high-temperature superconductivity.[71]

On 31 December 2023 "Global Room-Temperature Superconductivity in Graphite" was published in the journal Advanced Quantum Technologies, claiming to demonstrate superconductivity at room temperature and ambient pressure in highly oriented pyrolytic graphite with dense arrays of nearly parallel line defects.[36]

Nickelates

[edit | edit source]

In 1999, Anisimov et al. conjectured superconductivity in nickelates, proposing nickel oxides as direct analogs to the cuprate superconductors.[72] Superconductivity in an infinite-layer nickelate, Nd0.8Sr0.2NiO2, was reported at the end of 2019 with a superconducting transition temperature between Template:Cvt.[73][74] This superconducting phase is observed in oxygen-reduced thin films created by the pulsed laser deposition of Nd0.8Sr0.2NiO3 onto SrTiO3 substrates that is then reduced to Nd0.8Sr0.2NiO2 via annealing the thin films at 533–553 K (260–280 °C) in the presence of CaH2.[75] The superconducting phase is only observed in the oxygen reduced film and is not seen in oxygen reduced bulk material of the same stoichiometry, suggesting that the strain induced by the oxygen reduction of the Nd0.8Sr0.2NiO2 thin film changes the phase space to allow for superconductivity.[76] Of important is further to extract access hydrogen from the reduction with CaH2, otherwise topotactic hydrogen may prevent superconductivity. [77]

Production

[edit | edit source]

Liquid nitrogen can be produced relatively cheaply, even on-site. The higher temperatures additionally help to avoid some of the problems that arise at liquid helium temperatures, such as the formation of plugs of frozen air that can block cryogenic lines and cause unanticipated and potentially hazardous pressure buildup.[78][79]

Ongoing research

[edit | edit source]

The question of how superconductivity arises in high-temperature superconductors is one of the major unsolved problems of theoretical condensed matter physics. The mechanism that causes the electrons in these crystals to form pairs is not known. Despite intensive research and many promising leads, an explanation has so far eluded scientists. One reason for this is that the materials in question are generally very complex, multi-layered crystals (for example, BSCCO), making theoretical modelling difficult.

Improving the quality and variety of samples also gives rise to considerable research, both with the aim of improved characterisation of the physical properties of existing compounds, and synthesizing new materials, often with the hope of increasing Tc. Technological research focuses on making HTS materials in sufficient quantities to make their use economically viable[80] as well as in optimizing their properties in relation to applications.[81] LK-99, copper-doped lead-apatite, has also been proposed as a room-temperature superconductor.

In March 2026, University of Houston researchers reported a superconducting material exhibiting a critical temperature of approximately 151 K at ambient pressure.[82] This new record without sustained high-pressure conditions was achieved using a "pressure quenching" technique. This exceeded the previous ambient-pressure record of 133 K.

Theoretical models

[edit | edit source]

Multiple hypotheses attempt to account for HTS.

Resonating valence bond theory

[edit | edit source]
Main article: Resonating valence bond theory

Spin fluctuation hypothesis[83] proposed that electron pairing in high-temperature superconductors is mediated by short-range spin waves known as paramagnons.[84][85][dubious – discuss]

Gubser, Hartnoll, Herzog, and Horowitz proposed holographic superconductivity, which uses holographic duality or AdS/CFT correspondence theory as a possible explanation of high-temperature superconductivity in certain materials.[86]

Weak coupling theory suggests superconductivity emerges from antiferromagnetic spin fluctuations in a doped system.[87] It predicts that the pairing wave function of cuprate HTS should have a dx2-y2 symmetry. Thus, determining whether the pairing wave function has d-wave symmetry is essential to test the spin fluctuation mechanism. That is, if the HTS order parameter (a pairing wave function as in Ginzburg–Landau theory) does not have d-wave symmetry, then a pairing mechanism related to spin fluctuations can be ruled out. (Similar arguments can be made for iron-based superconductors but the different material properties allow a different pairing symmetry.)

Interlayer coupling theory proposes that a layered structure consisting of BCS-type (s-wave symmetry) superconductors can explain superconductivity by itself.[88] By introducing an additional tunnelling interaction between layers, this model explained the anisotropic symmetry of the order parameter as well as the emergence of HTS.

In order to resolve this question, experiments such as photoemission spectroscopy, NMR, specific heat measurements, were conducted. The results remain ambiguous, with some reports supporting d symmetry, with others supporting s symmetry.

Such explanations assume that superconductive properties can be treated by mean-field theory. It also does not consider that in addition to the superconductive gap, the pseudogap must be explained. The cuprate layers are insulating, and the superconductors are doped with interlayer impurities to make them metallic.

The transition temperature can be maximized by varying the dopant concentration. The simplest example is La2CuO4, which consists of alternating CuO2 and LaO layers that are insulating when pure. When 8% of the La is replaced by Sr, the latter acts as a dopant, contributing holes to the CuO2 layers, and making the sample metallic. The Sr impurities also act as electronic bridges, enabling interlayer coupling. Proceeding from this picture, some theories argue that the pairing interaction is with phonons, as in conventional superconductors with Cooper pairs. While the undoped materials are antiferromagnetic, even a few percent of impurity dopants introduce a smaller pseudogap in the CuO2 planes that is also caused by phonons. The gap decreases with increasing charge carriers, and as it nears the superconductive gap, the latter reaches its maximum. The transition temperature is then argued to be due to the percolating behaviour of the carriers, which follow zig-zag percolative paths, largely in metallic domains in the CuO2 planes, until blocked by charge density wave domain walls, where they use dopant bridges to cross over to a metallic domain of an adjacent CuO2 plane. The transition temperature maxima are reached when the host lattice has weak bond-bending forces, which produce strong electron–phonon interactions at the interlayer dopants.[89]

D symmetry in YBCO

[edit | edit source]
File:Meissner effect p1390048.jpg
Small magnet levitating above a high-temperature superconductor cooled by liquid nitrogen: this is a case of Meissner effect.

An experiment based on flux quantization of a three-grain ring of YBa2Cu3O7 (YBCO) was proposed to test the symmetry of the order parameter in the HTS. The symmetry of the order parameter could best be probed at the junction interface as the Cooper pairs tunnel across a Josephson junction or weak link.[90] It was expected that a half-integer flux, that is, a spontaneous magnetization could only occur for a junction of d symmetry superconductors. But, even if the junction experiment is the strongest method to determine the symmetry of the HTS order parameter, the results have been ambiguous. John R. Kirtley and C. C. Tsuei thought that the ambiguous results came from the defects inside the HTS, leading them to an experiment where both clean limit (no defects) and dirty limit (maximal defects) were considered simultaneously.[91] Spontaneous magnetization was clearly observed in YBCO, which supported the d symmetry of the order parameter in YBCO. But, since YBCO is orthorhombic, it might inherently have an admixture of s symmetry. By tuning their technique, they found an admixture of s symmetry in YBCO within about 3%.[92] Also, they found a pure dx2−y2 order parameter symmetry in tetragonal Tl2Ba2CuO6.[93]

Spin-fluctuation mechanism

[edit | edit source]

The lack of exact theoretical computations on such strongly interacting electron systems has complicated attempts to validate spin-fluctuation. However, most theoretical calculations, including phenomenological and diagrammatic approaches, converge on magnetic fluctuations as the pairing mechanism.

Qualitative explanation

[edit | edit source]

In a superconductor, the flow of electrons cannot be resolved into individual electrons, but instead consists of pairs of bound electrons, called Cooper pairs. In conventional superconductors, these pairs are formed when an electron moving through the material distorts the surrounding crystal lattice, which attracts another electron and forms a bound pair. This is sometimes called the "water bed" effect. Each Cooper pair requires a certain minimum energy to be displaced, and if the thermal fluctuations in the crystal lattice are smaller than this energy the pair can flow without dissipating energy. Electron flow without resistance is superconductivity.

In a high-Tc superconductor, the mechanism is extremely similar to a conventional superconductor, except that phonons play virtually no role, replaced by spin-density waves. Just as all known conventional superconductors are strong phonon systems, all known high-Tc superconductors are strong spin-density wave systems, within close vicinity of a magnetic transition to, for example, an antiferromagnet. When an electron moves in a high-Tc superconductor, its spin creates a spin-density wave around it. This spin-density wave in turn causes a nearby electron to fall into the spin depression created by the first electron (water-bed). When the system temperature is lowered, more spin density waves and Cooper pairs are created, eventually leading to superconductivity. High-Tc systems are magnetic systems due to the Coulomb interaction, creating a strong Coulomb repulsion between electrons. This repulsion prevents pairing of the Cooper pairs on the same lattice site. Instead, pairing occurs at near-neighbor lattice sites. This is the so-called d-wave pairing, where the pairing state has a node (zero) at the origin.

Examples

[edit | edit source]
Main article: List of superconductors

Examples of high-Tc cuprate superconductors include YBCO and BSCCO, which are the most known materials that achieve superconductivity above the boiling point of liquid nitrogen.

Temperatures of most practical superconductors and coolants, at ordinary pressures
Transition temperature Item Material type
Template:Cvt Dry ice (Carbon dioxide) – sublimation Coolant
Template:Cvt Lowest temperature recorded on Earth Coolant
Template:Cvt BSCCO Cuprate superconductors
Template:Cvt YBCO
Template:Cvt Nitrogen – Boiling Coolant
Template:Cvt SmFeAs(O,F) Iron-based superconductors
Template:Cvt CeFeAs(O,F)
Template:Cvt LaFeAs(O,F)
Template:Cvt Nb3Sn Metallic low-temperature superconductors
3K (−270 °C) Helium – boiling Coolant
Template:Cvt Hg (mercury: the first discovered superconductor) Metallic low-temperature superconductors

See also

[edit | edit source]

References

[edit | edit source]
  1. ↑ Timmer, John (May 2011). "25 years on, the search for higher-temp superconductors continues". Ars Technica. Archived from the original on 4 March 2012. Retrieved 2 March 2012.
  2. ↑ 2.0 2.1 Saunders, P. J.; Ford, G. A. (2005). The Rise of the Superconductors. Boca Raton, FL: CRC Press. ISBN 0-7484-0772-3.
  3. ↑ Bednorz, J. G.; Müller, K. A. (1986). "Possible high Tc superconductivity in the Ba-La-Cu-O system". Zeitschrift für Physik B. 64 (2): 189–193. Bibcode:1986ZPhyB..64..189B. doi:10.1007/BF01303701. S2CID 118314311.
  4. ↑ Wu, M. K.; Ashburn, J. R.; Torng, C. J.; Hor, P. H.; Meng, R. L.; Gao, L; Huang, Z. J.; Wang, Y. Q.; Chu, C. W. (1987). "Superconductivity at 93 K in a New Mixed-Phase Y–Ba–Cu–O Compound System at Ambient Pressure". Physical Review Letters. 58 (9): 908–910. Bibcode:1987PhRvL..58..908W. doi:10.1103/PhysRevLett.58.908. PMID 10035069.
  5. ↑ "1987: J. Georg Bednorz, K. Alex Müller". Nobelprize.org. The Nobel Prize in Physics. Archived from the original on 19 September 2008. Retrieved 19 April 2012.
  6. ↑ Plakida, N. (2010). High Temperature Cuprate Superconductors. Springer Series in Solid-State Sciences. Springer. p. 480. ISBN 978-3-642-12632-1.
  7. ↑ Choi, Charles Q. "A New Iron Age: New class of superconductor may help pin down mysterious physics". Scientific American. Retrieved 25 October 2019.
  8. ↑ 8.0 8.1 Lua error in package.lua at line 80: module 'Module:Citation/CS1/Suggestions' not found.
  9. ↑ Nisbett, Alec (producer) (1988). Superconductor: The race for the prize (Television Episode).
  10. ↑ Mourachkine, A. (2004). Room-Temperature Superconductivity. Cambridge, UK: Cambridge International Science Publishing. arXiv:cond-mat/0606187. Bibcode:2006cond.mat..6187M. ISBN 1-904602-27-4. cond–mat/0606187.
  11. ↑ Bednorz, J. G. & Müller, K. A. (1986). "Possible high Tc superconductivity in the Ba−La−Cu−O system". Z. Phys. B. 64 (1): 189–193. Bibcode:1986ZPhyB..64..189B. doi:10.1007/BF01303701. S2CID 118314311.
  12. ↑ Wu, M. K.; et al. (1987). "Superconductivity at 93 K in a New Mixed-Phase Y–Ba–Cu–O Compound System at Ambient Pressure". Physical Review Letters. 58 (9): 908–910. Bibcode:1987PhRvL..58..908W. doi:10.1103/PhysRevLett.58.908. PMID 10035069.
  13. ↑ Wolf, Stuart A.; Kresin, Vladimir Z., eds. (6 December 2012) [1987]. [[[:Template:GBurl]] Novel Superconductivity] Check |url= value (help). New York: Plenum Press. ISBN 978-1-4613-1937-5. Retrieved 2 August 2023.
  14. ↑ Tanaka, Shoji (2001). "High temperature superconductivity: History and Outlook" (PDF). JSAP International. Archived (PDF) from the original on 16 August 2012. Retrieved 2 March 2012.
  15. ↑ Anderson, Philip (1987). "The Resonating Valence Bond State in La2CuO4 and Superconductivity". Science. 235 (4793): 1196–1198. Bibcode:1987Sci...235.1196A. doi:10.1126/science.235.4793.1196. PMID 17818979. S2CID 28146486.
  16. ↑ Bickers, N. E.; Scalapino, D. J.; Scalettar, R. T. (1987). "CDW and SDW mediated pairing interactions". Int. J. Mod. Phys. B. 1 (3n04): 687–695. Bibcode:1987IJMPB...1..687B. doi:10.1142/S0217979287001079.
  17. ↑ Inui, Masahiko; Doniach, Sebastian; Hirschfeld, Peter J.; Ruckenstein, Andrei E.; Zhao, Z.; Yang, Q.; Ni, Y.; Liu, G. (1988). "Coexistence of antiferromagnetism and superconductivity in a mean-field theory of high-Tc superconductors". Phys. Rev. B. 37 (10): 5182–5185. Bibcode:1988PhRvB..37.5182D. doi:10.1103/PhysRevB.37.5182. PMID 9943697. Archived from the original on 3 July 2013.
  18. ↑ Gros, Claudius; Poilblanc, Didier; Rice, T. Maurice; Zhang, F. C. (1988). "Superconductivity in correlated wavefunctions". Physica C. 153–155: 543–548. Bibcode:1988PhyC..153..543G. doi:10.1016/0921-4534(88)90715-0.
  19. ↑ Kotliar, Gabriel; Liu, Jialin (1988). "Superexchange mechanism and d-wave superconductivity". Physical Review B. 38 (7): 5142–5145. Bibcode:1988PhRvB..38.5142K. doi:10.1103/PhysRevB.38.5142. PMID 9946940.
  20. ↑ Kamihara, Yoichi; Hiramatsu, Hidenori; Hirano, Masahiro; Kawamura, Ryuto; Yanagi, Hiroshi; Kamiya, Toshio; Hosono, Hideo (1 August 2006). "Iron-Based Layered Superconductor:  LaOFeP". Journal of the American Chemical Society. 128 (31): 10012–10013. doi:10.1021/ja063355c. ISSN 0002-7863.
  21. ↑ Bussmann-Holder, Annette; Keller, Hugo (1 February 2020). "High-temperature superconductors: underlying physics and applications". Zeitschrift für Naturforschung B. 75 (1–2): 3–14. arXiv:1911.02303. doi:10.1515/znb-2019-0103. ISSN 1865-7117.
  22. ↑ Dalla Piazza, B.; Mourigal, M.; Christensen, N. B.; Nilsen, G. J.; Tregenna-Piggott, P.; Perring, T. G.; et al. (2015). "Fractional excitations in the square-lattice quantum antiferromagnet". Nature Physics. 11 (1): 62–68. arXiv:1501.01767. Bibcode:2015NatPh..11...62D. doi:10.1038/nphys3172. PMC 4340518. PMID 25729400.
  23. ↑ "How electrons split: New evidence of exotic behaviors". Nanowerk (Press release). École Polytechnique Fédérale de Lausanne. 23 December 2014. Archived from the original on 23 December 2014. Retrieved 23 December 2014.
  24. ↑ Li, Yinwei; Hao, Jian; Liu, Hanyu; Li, Yanling; Ma, Yanming (7 May 2014). "The metallization and superconductivity of dense hydrogen sulfide". The Journal of Chemical Physics. 140 (17): 174712. arXiv:1402.2721. Bibcode:2014JChPh.140q4712L. doi:10.1063/1.4874158. ISSN 0021-9606. PMID 24811660. S2CID 15633660.
  25. ↑ Drozdov, A. P.; Eremets, M. I.; Troyan, I. A.; Ksenofontov, V.; Shylin, S. I. (2015). "Conventional superconductivity at 203 kelvin at high pressures in the sulfur hydride system". Nature. 525 (7567): 73–6. arXiv:1506.08190. Bibcode:2015Natur.525...73D. doi:10.1038/nature14964. ISSN 0028-0836. PMID 26280333. S2CID 4468914.
  26. ↑ 26.0 26.1 Wood, Charlie (14 October 2020). "Room-Temperature Superconductivity Achieved for the First Time". Quanta Magazine. Retrieved 29 October 2020.
  27. ↑ Cao, Yuan; Fatemi, Valla; Demir, Ahmet; Fang, Shiang; Tomarken, Spencer L.; Luo, Jason Y.; Sanchez-Yamagishi, J. D.; Watanabe, K.; Taniguchi, T. (5 March 2018). "Correlated insulator behaviour at half-filling in magic-angle graphene superlattices". Nature. 556 (7699): 80–84. arXiv:1802.00553. Bibcode:2018Natur.556...80C. doi:10.1038/nature26154. ISSN 1476-4687. PMID 29512654. S2CID 4601086.
  28. ↑ Wood, Charlie (16 March 2021). "A New Twist Reveals Superconductivity's Secrets". Quanta Magazine. Retrieved 23 March 2021.
  29. ↑ Drozdov, A. P.; Kong, P. P.; Minkov, V. S.; Besedin, S. P.; Kuzovnikov, M. A.; Mozaffari, S.; Balicas, L.; Balakirev, F. F.; Graf, D. E.; Prakapenka, V. B.; Greenberg, E.; Knyazev, D. A.; Tkacz, M.; Eremets, M. I. (2019). "Superconductivity at 250 K in Lanthanum Hydride under High Pressures". Nature. 569 (7757): 528–531. arXiv:1812.01561. Bibcode:2019Natur.569..528D. doi:10.1038/s41586-019-1201-8. PMID 31118520. S2CID 119231000.
  30. ↑ Snider, Eliot; et al. (14 October 2020). "Room-temperature superconductivity in a carbonaceous sulfur hydride". Nature. 586 (7829): 373–377. Bibcode:2020Natur.586..373S. doi:10.1038/s41586-020-2801-z. OSTI 1673473. PMID 33057222. S2CID 222823227.Template:Retracted
  31. ↑ Chang, Kenneth (14 October 2020). "Finally, the First Room-Temperature Superconductor". The New York Times.
  32. ↑ Snider, Elliot; Dasenbrock-Gammon, Nathan; McBride, Raymond; Debessai, Mathew; Vindana, Hiranya; Vencatasamy, Kevin; Lawler, Keith V.; Salamat, Ashkan; Dias, Ranga P. (26 September 2022). "Retraction Note: Room-temperature superconductivity in a carbonaceous sulfur hydride". Nature. 610 (7933): 804. Bibcode:2022Natur.610..804S. doi:10.1038/s41586-022-05294-9. PMID 36163290 Check |pmid= value (help). S2CID 252544156 Check |s2cid= value (help).
  33. ↑ 33.0 33.1 Cao, Qing; Grote, Fabian; Hußmann, Marleen; Eigler, Siegfried (2021). "Emerging field of few-layered intercalated 2D materials". Nanoscale Advances. 3 (4): 963–982. Bibcode:2021NanoA...3..963C. doi:10.1039/d0na00987c. PMC 9417328 Check |pmc= value (help). PMID 36133283 Check |pmid= value (help).
  34. ↑ Schilling, A.; Cantoni, M.; Guo, J. D.; Ott, H. R. (1993). "Superconductivity in the Hg–Ba–Ca–Cu–O system". Nature. 363 (6424): 56–58. Bibcode:1993Natur.363...56S. doi:10.1038/363056a0. S2CID 4328716.
  35. ↑ Drozdov, A. P.; Kong, P. P.; Minkov, V. S.; Besedin, S. P.; Kuzovnikov, M. A.; Mozaffari, S.; Balicas, L.; Balakirev, F. F.; Graf, D. E.; Prakapenka, V. B.; Greenberg, E.; Knyazev, D. A.; Tkacz, M.; Eremets, M. I. (2019). "Superconductivity at 250 K in lanthanum hydride under high pressures". Nature. 569 (7757): 528–531. arXiv:1812.01561. Bibcode:2019Natur.569..528D. doi:10.1038/s41586-019-1201-8. PMID 31118520. S2CID 119231000.
  36. ↑ 36.0 36.1 Kopelevich, Yakov; Torres, José; Da Silva, Robson; Oliveira, Felipe; Diamantini, Maria Cristina; Trugenberger, Carlo; Vinokur, Valerii (2024). "Global Room-Temperature Superconductivity in Graphite". Advanced Quantum Technologies. 7 (2). arXiv:2208.00854. doi:10.1002/qute.202300230.
  37. ↑ Report about first room-temperature (15 °C) superconductor H2S + CH4 at 267 GPa is not reliable (retracted). See Castelvecchi, Davide (27 September 2022). "Room-Stunning room-temperature-superconductor claim is retracted". Nature. doi:10.1038/d41586-022-03066-z. PMID 36171305 Check |pmid= value (help). S2CID 252597663 Check |s2cid= value (help).
  38. ↑ Eremets, M. I.; Minkov, V. S.; Drozdov, A. P.; Kong, P. P.; Ksenofontov, V.; Shylin, S. I.; Bud'ko, S. L.; Prozorov, R.; Balakirev, F. F.; Sun, Dan; Mozzafari, S.; Balicas, L. (10 January 2022). "High‑Temperature Superconductivity in Hydrides: Experimental Evidence and Details". Journal of Superconductivity and Novel Magnetism. 35 (4): 965–977. arXiv:2201.05137. doi:10.1007/s10948-022-06148-1.
  39. ↑ Drozdov, A. P.; Eremets, M. I.; Troyan, I. A.; Ksenofontov, V.; Shylin, S. I. (September 2015). "Conventional superconductivity at 203 kelvin at high pressures in the sulfur hydride system". Nature. 525 (7567): 73–76. arXiv:1506.08190. Bibcode:2015Natur.525...73D. doi:10.1038/nature14964. ISSN 0028-0836. PMID 26280333. S2CID 4468914.
  40. ↑ "Ambient-pressure 151-K superconductivity in HgBa2Ca2Cu3O8+δ via pressure quench". PNAS. 123 (11). 9 March 2026. arXiv:2603.12437. doi:10.1073/pnas.2536178123. Retrieved 15 March 2026.
  41. ↑ 41.0 41.1 "Superconductivity Examples". hyperphysics.phy-astr.gsu.edu. Retrieved 14 June 2020.
  42. ↑ Flükiger, R.; Hariharan, S.Y.; Küntzler, R.; Luo, H.L.; Weiss, F.; Wolf, T.; Xu, J.Q. (1994). "Nb–Ti". In Flükiger, R.; Klose, W. (eds.). Materials. 21b2: Nb–H – Nb–Zr, Nd–Np. Berlin; Heidelberg: Springer-Verlag. pp. 222–229. doi:10.1007/10423690_53. ISBN 3-540-57541-3. Retrieved 14 June 2020.
  43. ↑ 43.0 43.1 Kittel, Charles (1996). Introduction to Solid State Physics (7th ed.). New York, NY: Wiley. ISBN 0-471-11181-3. OCLC 32468930.
  44. ↑ Norman, Michael R. (2008). "Trend: High-temperature superconductivity in the iron pnictides". Physics. 1 (21): 21. Bibcode:2008PhyOJ...1...21N. doi:10.1103/Physics.1.21.
  45. ↑ "High-Temperature Superconductivity: The Cuprates". Devereaux group. Stanford University. Archived from the original on 15 June 2010. Retrieved 30 March 2012.
  46. ↑ Graser, S.; Hirschfeld, P. J.; Kopp, T.; Gutser, R.; Andersen, B. M.; Mannhart, J. (27 June 2010). "How grain boundaries limit supercurrents in high-temperature superconductors". Nature Physics. 6 (8): 609–614. arXiv:0912.4191. Bibcode:2010NatPh...6..609G. doi:10.1038/nphys1687. S2CID 118624779.
  47. ↑ Lua error in package.lua at line 80: module 'Module:Citation/CS1/Suggestions' not found.
  48. ↑ 48.0 48.1 Kordyuk, A. A. (2012). "Iron-based superconductors: Magnetism, superconductivity, and electronic structure (Review Article)" (PDF). Low Temp. Phys. 38 (9): 888–899. arXiv:1209.0140. Bibcode:2012LTP....38..888K. doi:10.1063/1.4752092. S2CID 117139280. Archived (PDF) from the original on 11 May 2015.
  49. ↑ Kamihara, Y.; Hiramatsu, H.; Hirano, M.; Kawamura, R.; Yanagi, H.; Kamiya, T.; Hosono, H. (2006). "Iron-based layered superconductor: LaOFeP". Journal of the American Chemical Society. 128 (31): 10012–10013. Bibcode:2006JAChS.12810012K. doi:10.1021/ja063355c. PMID 16881620.
  50. ↑ Kamihara, Y.; Watanabe, T.; Hirano, M.; Hosono, H. (2008). "Iron-Based Layered Superconductor La[O1−xFx]FeAs (x=0.05–0.12) with Tc = 26 K". Journal of the American Chemical Society. 130 (11): 3296–3297. doi:10.1021/ja800073m. PMID 18293989.
  51. ↑ Takahashi, H.; Igawa, K.; Arii, K.; Kamihara, Y.; Hirano, M.; Hosono, H. (2008). "Superconductivity at 43 K in an iron-based layered compound LaO1-xFxFeAs". Nature. 453 (7193): 376–378. Bibcode:2008Natur.453..376T. doi:10.1038/nature06972. PMID 18432191. S2CID 498756.
  52. ↑ Lua error in package.lua at line 80: module 'Module:Citation/CS1/Suggestions' not found.
  53. ↑ Liu, Defa; Zhang, Wenhao; Mou, Daixiang; He, Junfeng; Ou, Yun-Bo; Wang, Qing-Yan; et al. (2012). "Electronic origin of high-temperature superconductivity in single-layer FeSe superconductor". Nat. Commun. 3 (931): 931. arXiv:1202.5849. Bibcode:2012NatCo...3..931L. doi:10.1038/ncomms1946. PMID 22760630. S2CID 36598762.
  54. ↑ He, Shaolong; He, Junfeng; Zhang, Wenhao; Zhao, Lin; Liu, Defa; Liu, Xu; et al. (2013). "Phase diagram and electronic indication of high-temperature superconductivity at 65 K in single-layer FeSe films". Nat. Mater. 12 (7): 605–610. arXiv:1207.6823. Bibcode:2013NatMa..12..605H. doi:10.1038/NMAT3648. PMID 23708329. S2CID 119185689.
  55. ↑ Ge, J. F.; Liu, Z. L.; Liu, C.; Gao, C. L.; Qian, D.; Xue, Q. K.; Liu, Y.; Jia, J. F. (2014). "Superconductivity in single-layer films of FeSe with a transition temperature above 100 K". Nature Materials. 1406 (3): 285–9. arXiv:1406.3435. Bibcode:2015NatMa..14..285G. doi:10.1038/nmat4153. PMID 25419814. S2CID 119227626.
  56. ↑ Lua error in package.lua at line 80: module 'Module:Citation/CS1/Suggestions' not found.
  57. ↑ Lua error in package.lua at line 80: module 'Module:Citation/CS1/Suggestions' not found.
  58. ↑ Lua error in package.lua at line 80: module 'Module:Citation/CS1/Suggestions' not found.
  59. ↑ Pitcher, M. J.; Parker, D. R.; Adamson, P.; Herkelrath, S. J.; Boothroyd, A. T.; Ibberson, R. M.; Brunelli, M.; Clarke, S. J. (2008). "Structure and superconductivity of LiFeAs". Chemical Communications. 2008 (45): 5918–5920. arXiv:0807.2228. doi:10.1039/b813153h. PMID 19030538. S2CID 3258249.
  60. ↑ Lua error in package.lua at line 80: module 'Module:Citation/CS1/Suggestions' not found.
  61. ↑ Parker, D. R.; Pitcher, M. J.; Baker, P. J.; Franke, I.; Lancaster, T.; Blundell, S. J.; Clarke, S. J. (2009). "Structure, antiferromagnetism and superconductivity of the layered iron arsenide NaFeAs". Chemical Communications. 2009 (16): 2189–2191. arXiv:0810.3214. doi:10.1039/b818911k. PMID 19360189. S2CID 45189652.
  62. ↑ Hsu, F. C.; Luo, J. Y.; Yeh, K. W.; Chen, T. K.; Huang, T. W.; Wu, P. M.; et al. (2008). "Superconductivity in the PbO-type structure α-FeSe". Proceedings of the National Academy of Sciences of the United States of America. 105 (38): 14262–14264. Bibcode:2008PNAS..10514262H. doi:10.1073/pnas.0807325105. PMC 2531064. PMID 18776050.
  63. ↑ Lua error in package.lua at line 80: module 'Module:Citation/CS1/Suggestions' not found.
  64. ↑ Hansen, M. F.; et al. (2022). "Superconductivity in the crystallogenide LaFeSiO1−δ with squeezed FeSi layers". npj Quantum Materials. 7: 86. arXiv:2206.11690. doi:10.1038/s41535-022-00493-z.
  65. ↑ Vaney, J. B.; et al. (2022). "Topotactic fluorination of intermetallics as an efficient route towards quantum materials". Nature Communications. 13: 1462. Bibcode:2022NatCo..13.1462V. doi:10.1038/s41467-022-29043-8. PMC 8933527 Check |pmc= value (help). PMID 35304455.
  66. ↑ Zhao, J.; Huang, Q.; de la Cruz, C.; Li, S.; Lynn, J. W.; Chen, Y.; et al. (2008). "Structural and magnetic phase diagram of CeFeAsO1−xFx and its relation to high-temperature superconductivity". Nature Materials. 7 (12): 953–959. arXiv:0806.2528. Bibcode:2008NatMa...7..953Z. doi:10.1038/nmat2315. PMID 18953342. S2CID 25937023.
  67. ↑ Lua error in package.lua at line 80: module 'Module:Citation/CS1/Suggestions' not found.
  68. ↑ Preuss, Paul. "A Most Unusual Superconductor and How It Works". Berkeley Lab. Archived from the original on 3 July 2012. Retrieved 12 March 2012.
  69. ↑ Hebard, A. F.; Rosseinsky, M. J.; Haddon, R. C.; Murphy, D. W.; Glarum, S. H.; Palstra, T. T. M.; Ramirez, A. P.; Kortan, A. R. (1991). "Superconductivity at 18 K in potassium-doped C60" (PDF). Nature. 350 (6319): 600–601. Bibcode:1991Natur.350..600H. doi:10.1038/350600a0. hdl:11370/3709b8a7-6fc1-4b32-8842-ce9b5355b5e4. S2CID 4350005.
  70. ↑ Ganin, A. Y.; Takabayashi, Y.; Khimyak, Y. Z.; Margadonna, S.; Tamai, A.; Rosseinsky, M. J.; Prassides, K. (2008). "Bulk superconductivity at 38 K in a molecular system". Nature Materials. 7 (5): 367–71. Bibcode:2008NatMa...7..367G. doi:10.1038/nmat2179. PMID 18425134.
  71. ↑ Lua error in package.lua at line 80: module 'Module:Citation/CS1/Suggestions' not found.
  72. ↑ Anisimov, V. I.; Bukhvalov, D.; Rice, T. M. (15 March 1999). "Electronic structure of possible nickelate analogs to the cuprates". Physical Review B. 59 (12): 7901–7906. Bibcode:1999PhRvB..59.7901A. doi:10.1103/PhysRevB.59.7901.
  73. ↑ Li, D.; Lee, K.; Wang, B. Y.; et al. (2019). "Superconductivity in an infinite-layer nickelate". Nature. 572 (7771): 624–627. Bibcode:2019Natur.572..624L. doi:10.1038/s41586-019-1496-5. OSTI 1562463. PMID 31462797. S2CID 201656573.
  74. ↑ Botana, A. S.; Bernardini, F.; Cano, A. (2021). "Nickelate superconductors: an ongoing dialog between theory and experiments". Journal of Experimental and Theoretical Physics. 132 (4): 618–627. arXiv:2012.02764. Bibcode:2021JETP..132..618B. doi:10.1134/S1063776121040026. S2CID 255191342 Check |s2cid= value (help).
  75. ↑ Lua error in package.lua at line 80: module 'Module:Citation/CS1/Suggestions' not found.
  76. ↑ Li, Q.; He, C.; et al. (2020). "Absence of supercondutivity in bulk Nd1−xSrxNiO2". Communications Materials. 1 (1): 16. arXiv:1911.02420. Bibcode:2020CoMat...1...16L. doi:10.1038/s43246-020-0018-1. S2CID 208006588.
  77. ↑ Lua error in package.lua at line 80: module 'Module:Citation/CS1/Suggestions' not found.
  78. ↑ "Introduction to Liquid Helium". Cryogenics and Fluid Branch. Goddard Space Flight Center, NASA.
  79. ↑ "Section 4.1 'Air plug in the fill line'". Superconducting Rock Magnetometer Cryogenic System Manual. 2G Enterprises. Archived from the original on 6 May 2009. Retrieved 9 October 2012.
  80. ↑ Díez-Sierra, Javier; López-Domínguez, Pedro; Rijckaert, Hannes; Rikel, Mark; et al. (2021). "All-chemical YBa2Cu3O7- $\delta$ coated conductors with preformed BaHfO3 and BaZrO3 nanocrystals on Ni5W technical substrate at the industrial scale". Superconductor Science and Technology. 34 (11): 114001. Bibcode:2021SuScT..34k4001D. doi:10.1088/1361-6668/ac2495. hdl:1854/LU-8719549. S2CID 237591103.
  81. ↑ Díez-Sierra, Javier; López-Domínguez, Pedro; Rijckaert, Hannes; Rikel, Mark; Hänisch, Jens; Khan, Mukarram Zaman; et al. (2020). "High critical current density and enhanced pinning in superconducting films of YBa2Cu3O7−δ nanocomposites with embedded BaZrO3, BaHfO3, BaTiO3, and SrZrO3 nanocrystals". ACS Applied Nano Materials. 3 (6): 5542–5553. doi:10.1021/acsanm.0c00814. hdl:1854/LU-8661998. S2CID 219429094.
  82. ↑ Adkison, Michael (17 March 2026). "These UH professors broke a record for superconductivity. They say it could change how we transmit energy". Houston Public Media. Retrieved 23 March 2026.
  83. ↑ Mann, Adam (20 July 2011). "High-temperature superconductivity at 25: Still in suspense". Nature. 475 (7356): 280–2. Bibcode:2011Natur.475..280M. doi:10.1038/475280a. PMID 21776057. S2CID 205066154.
  84. ↑ Pines, D. (2002), "The Spin Fluctuation Model for High Temperature Superconductivity: Progress and Prospects", The Gap Symmetry and Fluctuations in High-Tc Superconductors, NATO Science Series: B, 371, New York: Kluwer Academic, pp. 111–142, doi:10.1007/0-306-47081-0_7, ISBN 978-0-306-45934-4
  85. ↑ Monthoux, P.; Balatsky, A. V. & Pines, D. (1991). "Toward a theory of high-temperature superconductivity in the antiferromagnetically correlated cuprate oxides". Physical Review Letters. 67 (24): 3448–3451. Bibcode:1991PhRvL..67.3448M. doi:10.1103/PhysRevLett.67.3448. PMID 10044736.
  86. ↑ Jan Zaanen, Yan Liu, Ya Sun K.Schalm (2015). Holographic Duality in Condensed Matter Physics. Cambridge University Press, Cambridge.
  87. ↑ Monthoux, P.; Balatsky, A.; Pines, D. (1992). "Weak-coupling theory of high-temperature superconductivity in the antiferromagnetically correlated copper oxides". Physical Review B. 46 (22): 14803–14817. Bibcode:1992PhRvB..4614803M. doi:10.1103/PhysRevB.46.14803. PMID 10003579.
  88. ↑ Chakravarty, S.; Sudbø, A.; Anderson, P. W.; Strong, S. (1993). "Interlayer Tunneling and Gap Anisotropy in High-Temperature Superconductors". Science. 261 (5119): 337–340. Bibcode:1993Sci...261..337C. doi:10.1126/science.261.5119.337. PMID 17836845. S2CID 41404478.
  89. ↑ Phillips, J. (2010). "Percolative theories of strongly disordered ceramic high-temperature superconductors". Proceedings of the National Academy of Sciences of the United States of America. 43 (4): 1307–10. Bibcode:2010PNAS..107.1307P. doi:10.1073/pnas.0913002107. PMC 2824359. PMID 20080578.
  90. ↑ Geshkenbein, V.; Larkin, A.; Barone, A. (1987). "Vortices with half magnetic flux quanta in heavy-fermion superconductors". Physical Review B. 36 (1): 235–238. Bibcode:1987PhRvB..36..235G. doi:10.1103/PhysRevB.36.235. PMID 9942041.
  91. ↑ Kirtley, J. R.; Tsuei, C. C.; Sun, J. Z.; Chi, C. C.; Yu-Jahnes, Lock See; Gupta, A.; Rupp, M.; Ketchen, M. B. (1995). "Symmetry of the order parameter in the high-Tc superconductor YBa2Cu3O7−δ". Nature. 373 (6511): 225–228. Bibcode:1995Natur.373..225K. doi:10.1038/373225a0. S2CID 4237450.
  92. ↑ Kirtley, J. R.; Tsuei, C. C.; Ariando, A.; Verwijs, C. J. M.; Harkema, S.; Hilgenkamp, H. (2006). "Angle-resolved phase-sensitive determination of the in-plane gap symmetry in YBa2Cu3O7−δ" (PDF). Nature Physics. 2 (3): 190–194. Bibcode:2006NatPh...2..190K. doi:10.1038/nphys215. S2CID 118447968.
  93. ↑ Tsuei, C. C.; Kirtley, J. R.; Ren, Z. F.; Wang, J. H.; Raffy, H.; Li, Z. Z. (1997). "Pure dx2−y2 order-parameter symmetry in the tetragonal superconductor Tl2Ba2CuO6+δ". Nature. 387 (6632): 481–483. Bibcode:1997Natur.387..481T. doi:10.1038/387481a0. S2CID 4314494.
[edit | edit source]

Template:Emerging technologies Template:Superconductivity

Retrieved from "https://wiki.tachyony.co.uk/w/index.php?title=High-temperature_superconductivity"